refractory brick

What are the unique advantages of Sillimanite Brick?

07:58, 19/9/2016 .. 0 comments .. Link

Sillimanite brick is refractory brick made of sillimanite minerals. Commonly using high temperature burning method and mud casting method to product.

Sillimanite brick has five big advantage of using:

1. The application of non-ferrous metal smelting industry

Use silicon carbid, high temperature resistance, big strength, good heat conduction performance, impact resistance, high-temperature indirect heating material, such as strong retort furnace. Distillation furnace tray, aluminium electrolyzer, copper melting furnace lining, furnace zinc powder with arc plate, the thermocouple protection tube, etc.

2. The application of iron and steel industry

The use of silicon carbide corrosion resistance. Thermal shock resistance to wear and tear. Good characteristics of thermal conductivity, for large blast furnace lining to improve the service life.

3. The application of metallurgical mineral processing industry

Silicon carbide hardness is second only to diamond, strong wear resistance, is wear-resisting pipe, the impeller, pump room, cyclone, ore bucket lined with ideal material, its wear resistance is  5 to 20 times than the service life of cast iron,rubber,  is one of the aviation flight track ideal material.

4. The application of building materials ceramic, grinding wheel industry

Using the coefficient of thermal conductivity.The characteristics of thermal radiation, high strength, manufacturing sheet kiln furniture, not only can reduce the capacity of kiln furniture, also improves the loading capacity of the kiln and the product quality, shorten the production cycle, is the ideal indirect materials of ceramic glaze baking sintering.



The characteristics and application scope of Ceramic Fiber Board

02:54, 18/9/2016 .. 0 comments .. Link

Characteristics

Ceramic fiber board product quality of a material is solid, good toughness and strength, has excellent ability to resist wind erosion. Heating is not inflation, qualitative light, construction is convenient, can be arbitrary bending shear,

is ideal energy-saving materials of kiln, pipe and other insulation equipment.

1. High crushing strength, long service life.

2. Low thermal capacity, low thermal conductivity.

3. Non- brittle material, good toughness.

4. Size precision, good flatness.

5. Easily cut installation, construction is convenient.

6. Excellent resistance to wind erosion performance.

7. Continuous production, uniform fiber distribution, stable performance.

Application scope

1. The back lining of cement building materials industry kiln keep warm.

2. Petrochemical, metallurgy, ceramics, glass industry kiln back lining keep warm.

3. Heat treatment furnace back lining keep warm.

4. The non-ferrous metal industry back lining keep warm.



The Manufcturing Process Of Fire Clay Bricks

11:04, 11/5/2016 .. 0 comments .. Link

The manufcturing process of fire clay bricks includes seven steps.

1) Obtain raw materials. The clay for manufacturing bricks is obtained from the ancient soil deep under the earth’s surface. The soil in this layer is slightly deeper in color than the topsoil and was formed about 80,000 to 120,000 years ago. At that time, the climate is warm and humid and plants are diverse and lush , which mades the soil in this period soft and sticky and a good raw material for fire clay bricks.

2) The clay is stacked in the open air for up to six months to make its inner structure loose. Then it is crushed and screened to get the pure fine clay.

3) Add water to the clay and then repeat kneading to make it into thick mud. This step is very important for the finished products.

4) Puur the mud into the mold. Compact it and then remove the remaining mud with a wire bow.

5) Release the green body from the mold and dry it in the shadow to avoid cracks and deformation caused by exposure to the sun.

6) After drying, fire the bricks in the kiln. This process is the most important part of the brick-making process.

7) After ten days of firing, the green body is basically sintered. if stopping heating at this time, the outside air may come into the kiln and make the bricks oxidized into red bricks. in order to prevent oxidazing, seal the kiln roof with clay.



Four Factors For The Production Of Magnesia Carbon Brick

08:53, 9/5/2016 .. 0 comments .. Link

Magnesia carbon brick is mde of magnesium oxide (melting point 2800 ) and carbon material with a high melting point that is difficult to be infiltrated by slags by adding a variety of non-oxide additives. It is mainly used in the converter, AC arc furnace, DC arc furnace lining, ladle slag lines and other parts.

The factors for the production of magnesia carbon brick incldue raw materials, binding agents and additives.

1) Magnesia sand

Magnesia sand should have high purity. Compared to sintered magnesia brick, fused magnesia brick has more complete crystal structure and stable reducing effect on carbon, so the production of magnesai brick turns to fused magnesia bricks. Given the binding state of carbon and infiltration of binding agents, fused magnesia can be mixed with sintered magnesia.

Magnesia carbon brick made of magnesia sand with high MgO content, large periclase particles and a lime-silica ratio of greater than 2 has the best quality.

2) Graphite

Graphite is another raw material for magnesia carbon bricks. it has good basic refractory properties. It contains 85%-98% fixed carbon and 13%-2% ash nd has a relative density of 2.09-2.23 and a melting point of 3640K ( volatile).

There are three reasons for the oxidization of graphite during use:
a. Oxygen in the air
b. Oxides in the slag
c. Oxides in graphite itself

Oxide impurities can react with graphite and make the structure loose, permeability increased and strength reduced, which is the main reason for the damage of magnesia carbon brick. Therefore, graphite with high purity and large flake crystals is mainly used for the production of magnesia carbon brick.

3) Binding agent

Binding agent is important for magnesia carbon brick and other carbon refractory products. Graphite and refractory oxides are not miscible. Thwy rely on binding agents to bond. At high temperature, the binding agent will be carbonized and form carbon bond with graphite. These binding agents are typically phenolic resins, modified bitumen, petroleum cracking by-products. Among them, phenolic resin has the best performance.

4) Additives

During the damaging process of magnesia carbon bricks, the oxidization of graphite is the main reason. The oxidation and carbon loss result in loose structure and weak strenth. In order to improve the oxidation resistance of magnesia carbon bricks, a certain amount of additives are added, including silica powder, alumina powder, FeSi alloy, CaSi alloy, SiC, Si3N4 and B4C. another function of additives is to build a bridge between refractory oxides and graphite and reinforce the binding between refractory oxides and graphite.



How To Judge The Quality Of Fire Clay Brick

04:15, 18/4/2016 .. 0 comments .. Link

Fire clay brick accounts for an important position in the refractory industry. The most important feature of fire clay brick is that the raw materials can be obtainded locally.

Fire clay brick is cheap and durable. It can be used for fire protection, thermal insulation, sound insulation and moisture absorption. Therefore, it is widely used in industrial production. The scrap bricks can be reused as aggregate.

When purchasing fire clay bricks, some professional knowledge is needed and some principles should be followed.

1) Take your need into account, such as specifications and materials.

2) Select appropriate manufacturers. Shop around and capare the price before you buy. Also pay attention to the credibility of manufacturers, after sales service, product quality and service attitude.

3) After selecting a manufaturer, give a visit to the factory to understand the strength of manufacturers, scale, production qualification, production capacity and evaluation on the product from other customers.

4) Pay attention to the proper use of fire clay brick in the production and the implementation of safety measures so as to make full use of fire clay brick, reduce unnecessary losses, extend the service life ansd reduce the cost.



How to select fused cast AZS block

09:05, 13/4/2016 .. 0 comments .. Link

Recently, with the development of furnace technology, more and more fused cast AZS block is used in the glass furnace. So, how to select fused cast AZS block?

1) fused cast AZS 33# block is used in the sidewall in contact with glass liquid. In the upper part of the sidewall, WS AZS 44# block is the best choice.

2) PT fused cast AZS is enough in the upper part of the glass furnace.

3) In the insulated bottom, fused cast AZS WS 33# is suitable as the paving block and can be used with AZS ramming mass during the construction.

4) PT AZS 33# block made by the reducing method is used in the sidewall, flat arch and oblique arch of the small furnace.

5) PT α—β fused cast alumina block is generally used in the sidewall of the refining zone, while WSα—β fused cast alumina block is used in the bottom. However, fused cast alumina block is expensive, so 33# AZS block is used as an alternative.



The size and specification requirements for hot stove fire clay bricks

09:32, 5/4/2016 .. 0 comments .. Link

Hot stove fire clay brick is made of refractory clay as the raw material. It is used in the hot stove, regenerator and partition walls. It is required to have good thermal shock resistance, high softening temperature and low creep rate.

China Metallurgical standard (YB / T 5107-1993) classifies the hot stove fire clay brick into RN-42RN-40 and RN-36 3 according to the physical and chemical parameters.

There are the following provisions for the physical and chemical parameters and the allowable size deviation.

1) If the width is not more than 0.25mm, no limit to the length;

2) If the width is between 0.26-0.5mm, length should be no more than 30mm;

3) If the width is more than 0.5mm, not allowed.



The Use Of Silica Brick In The Glass Furnace

09:44, 29/3/2016 .. 0 comments .. Link

Since the silica brick has low price, high purity, high softening temperature under load, no pollution to glass liquid and good resistance to R2O gases and aicd gases, it is widely used in the crown of the glass furnace, the upper part of the suspended wall, the back wall and the front wall.

The SiO2 content in the silica brick used in the glass furnaces should be controlled. And it should be mainly composed of cristobalite. For large glass furnaces and oxy-fuel glass furnaces, refractory materials with high purity, good creep resistance and good corrosion resistance are used.

Since the advent of brick, there are three types of brick. The first is the common silica brick. the second is high quality silica brick. the third category is improved high quality silica brick.

With the development of glass mleting technology, silica bricks with better performance are required.



The Use Of Silica Brick In The Glass Furnace

09:44, 29/3/2016 .. 0 comments .. Link

Since the silica brick has low price, high purity, high softening temperature under load, no pollution to glass liquid and good resistance to R2O gases and aicd gases, it is widely used in the crown of the glass furnace, the upper part of the suspended wall, the back wall and the front wall.

The SiO2 content in the silica brick used in the glass furnaces should be controlled. And it should be mainly composed of cristobalite. For large glass furnaces and oxy-fuel glass furnaces, refractory materials with high purity, good creep resistance and good corrosion resistance are used.

Since the advent of brick, there are three types of brick. The first is the common silica brick. the second is high quality silica brick. the third category is improved high quality silica brick.

With the development of glass mleting technology, silica bricks with better performance are required.



The Use Of Silica Brick In The Glass Furnace

09:44, 29/3/2016 .. 0 comments .. Link

Since the silica brick has low price, high purity, high softening temperature under load, no pollution to glass liquid and good resistance to R2O gases and aicd gases, it is widely used in the crown of the glass furnace, the upper part of the suspended wall, the back wall and the front wall.

The SiO2 content in the silica brick used in the glass furnaces should be controlled. And it should be mainly composed of cristobalite. For large glass furnaces and oxy-fuel glass furnaces, refractory materials with high purity, good creep resistance and good corrosion resistance are used.

Since the advent of brick, there are three types of brick. The first is the common silica brick. the second is high quality silica brick. the third category is improved high quality silica brick.

With the development of glass mleting technology, silica bricks with better performance are required.



The Checker Work of Glass Furnaces

09:04, 25/3/2016 .. 0 comments .. Link

The checker work of glass furnaces is subjected to more serious corrosion than the crown and sidewall since all checker bricks are subjected to high temperature, duct and alkali vapor. The plugging and collapsing are the main reasons for the shutdown and cold repair of glass furnaces. Therefore, the refractory materials of the checker work should have high mechanical strength, low creep and good resistance to the changes in temperature and atmosphere and alkali corrosion and does not adsorb dust.

In the top part of the checker work, the temperature is high, which can reach up to 1400-1500. It is subjected to the most severe erosion by alkali vapor and dust. Rebonded fused magnesia brick is used here. Since rebonded fused magnesia brick contains less silicate phase, periclase crystals are fully developed and are directly bonded, which delays and deters the growing speed of the periclase crystals under the effect of alkali vapor and cracking and pulverizing of bricks.

In the upper part of the checker work, the temperature is 1100-1400. Rebonded magnesia brick 95 is used.

In the middle part of the checker work, the temperature is 800-1100, within which alkali metal sulfate is condensed and magnesium and calcium checker work severely eroded by Na2O and SO3. It is accompanied with large expansion of bricks and badly damaged. Therefore, the site should not use magnesia brick but direct bonded magnesia chrome brick, magnesia zirconia brick, synthetic magnesia olivine brick and magnesia alumina spinel brick.

In the lower part of the checker work, the temperature is low here and the corrosion is not quite severe. However, it is close to the flue and directly affected by cold air, so it should have good thermal shock resistance and low prices. low porosity fire clay brick is used here.



Applications of fire clay bricks

08:14, 22/3/2016 .. 0 comments .. Link

Fire clay brick plays a versatile role in the many industries.

Fire clay brick can be used in the metallurgical industry. Fire clay materials including shaped refractory materials and unshaped refractory materials acount for about 70% of the total refractory materials. Hard clay is used to produce refractory materials for theblast frunace, hot stove, ladle lining brick and plug brick.

High-alumina clay is used to produce alumina bricks for electric furnaces and blast furnaces, high aluminum lining brick and high alumina refractory mud. Hard clay and high alumina clay are often calcined into clinker at high temperature (1400 - 1800).

Refractory clay also has important roles in the grinding industry, chemical industry and ceramics industry. High-alumina clay can be made into abrasive materials by melting in an electric arc furnace. Fused corundum abrasive material is currently the most widely used an abrasive material. It acounts for 2/3 of the total abrasive materials.

High alumina clay can be used to produce a variety of aluminum compounds such as aluminum sulfate, aluminum hydroxide, aluminum chloride, aluminum potassium sulfate and other chemical products. In the ceramic industry, hard clay and semi-hard clay can be used to manufacture household porcelain, construction porcelain and industrial porcelain.

In the construction materials industry, refractory clay can be used to produce high alumina bricks, phosphate high alumina refractory bricks and high alumina fused cast bricks. High-alumina clay can be made into aluminum-containing cement by calcining and then mixing with limestone. This quick-setting cement has strogn heat and corrosion resistance.



The Composition and Properties of Magnesia Brick

04:38, 17/3/2016 .. 0 comments .. Link

Magnesia brick is a basic refractory product with periclase as its main mineral phase. It contains not less than 91% MgO and not less than 3.0% CaO.

Magnesia brick is composed of 80-90% periclase and 8%-20% other mineral phase including magnesium ferrite (MgO·Fe2O3), forsterite (2MgO · SiO2) and Calcium and magnesium olive stone (CaO·MgO·SiO2).Silicate glass contains about 3-5% magnesium, calcium and iron. These silicates may contain tricalcium silicate (3CaO · SiO2), magnesium rhodonite (3CaO · MgO · 2SiO2), calcium and magnesium olivine and forsterite, dicalcium silicate (2CaO · SiO2).

Magnesia brick has good thermal conductivity, good thermal expansion, good corrosion resistance to alkali molten slags and bad corrosion resistance to acid molten slags. Due to the low-melting silicate cements surrounded periclase, the beginning point of the softening temperature under load is not too high, but the collapse temperature is close to the beginning point. Its refractoriness is over 2000, but it does not make sense in the actual use. Bad thermal shock stability is one of the main reasons for the destruction.

In the storage and transport, special attention should be paid to moisture-proof to avoid burst after affected with damp.



The Application of Dense Zircon Brick in Glass Furnaces

08:46, 14/3/2016 .. 0 comments .. Link

Zircon is chemically inert with good erosion resistance to high temperature molten glass and slag solution. High dense zircon brick made of zircon powder as the main raw material has good high temperature strength and strong resistance to glass liquid, so it is widely used as the bottom paving block and back lining structure in the glass furnaces and the lining of the glass furnaces for producing glass fiber.

During the use, some parts of the glass furnace are required to have good thermal shock resistance. Since the thermal shock stability of the dense zircon brick is bad, it reduces the service life of glass furnaces and increases the repair cost of glass furnaces.

Zircon can improve the properties of dense zircon brick. The dense zircon brick is made of zircon powder by adding high pure industrial zirconia, fused stabilized zirconia and desilicated zirconia. After Formulating according to the amount of the added zirconia, wet-mixing, spray granulation, isostatic pressing and sintering at 1530 and 12h insulation, 69% dense zircon brick is made.

Research about these three different samples of zirconia on the apparent porosity, bulk density, firing shrinkage and thermal shock stability and a scanning electron microscope (SEM) on the microstructure and fracture surface samples are carried out.

The results showed that: compared to 65 dense zircon brick without ZrO2 added, the samples with ZrO2 added have higher apparent porosity, bulk density, firing shrinkage and thermal shock stability.



Applications of Fused Cast AZS Block

08:30, 8/3/2016 .. 0 comments .. Link

Fused cast AZS block is made of high pure raw materials in a special electric arc furnace by the casting process of long arc melting and oxidation treatment. There is almost no carbon contamination from the electrodes.

Due to the casting process and high pure materials, fused cast AZS block has super strong corrosion resistance to the glass liquid and low potential of pollution.

Fused cast AZS 33# block has great advantage in preventing the pollution from glass liquid. It can generate stones in glass and has low potential of glass precipitation and bubbling. It is suitable to the upper structure of the melting zone, the sidewall of the work tank, the paving blocks and the forehearth.

Fused cast AZS 36# block is the standard fused cast AZS block made by the oxidizing method. It has special high corrosion resistance to the glass liquid and has low potential of pollution. It is suitable for the areas that are in direct contact with the glass liquid, such as the sidewall of the melting zone, paving block and feed port.

Fused cast AZS 41# block is the highest grade fused cast AZS block. It has the best corrosion resistance to the glass liquid and low pollution potential. It is suitable for the parts that require super high resistance such as the electric melting furnace, throat, kiln dam, bubble block and the corner block of the feed port.



Chemical composition of fire clay bricks

09:00, 3/3/2016 .. 0 comments .. Link

Fire clay brick is the refractory brick containing 30-46% SiO2. It is made of clinkers calcined from refractory clays as the oxidant and bond clay as a binder agent.

The main raw material is refractory clay. Clay is an earthy mineral. It can form plastic mud pie when mixed with water and maintain the shape after drying. It has rock-like hardness after fired at high temperature.

Additionally, the clay contains a certain amount of impurities such as quartz, mica, pyrite, feldspar and organic substances. The impurities, especially iron, can reduce the quality of clay and are harmful to the fire clay bricks.

Alkalis such as Na2O and K2O exist as mica. It can improve the sintering properties of clay and form dense products after sintered. It should be fewer than 2%.

The content of CaO is generally under 11.5% and distributed evenly. So, it will not affect the refractory properties of raw materials.

There is a certain amount of TiO2 in the bond clay. It exists as diamond. When it is less than 1%, it has no big effect on the quality of bond clay. In the chemical analysis, its content is not tested alone but counted in the content of A1203 + TiO2.

When the impurities in the clay exceed 6%, the refractoriness of clay will decease and cannot be used as the raw materials. The content of organic substances in the clay is fluctuated greatly, up to 5%.



Properties and applications of fused cast AZS

08:18, 1/3/2016 .. 0 comments .. Link

Fused cast AZS block is the most widely used fused cast refractory brick. According to the ZrO2 content, it can be divided into 33#, 36# and 41#AZS.

Fused cast AZS containing 33% ZrO2 is called 33# fused cast AZS; fused cast AZS containing 36% ZrO2 is called 36# fused cast AZS; fused cast AZS containing 41% ZrO2 is called 41# fused cast AZS.

Fused cast AZS is mainly composed of baddeleyite and corundum and their eutectic crystals. High viscosity glass phase is filled in the gaps of crystals. The crystals is directly precipitated from the molten liquid and well developed. So, it has large crystal particles and stable crystal phase. Except the voids, it has compact structure and better density than the common sintered bricks. The pores are mainly closed pores and the crystals are intertwined each other, so it has good mechanical properties and wear resistance. The impurities are difficult to invade the bricks. Therefore, this refractory brick has good corrosion resistance. besides, the transformation of ZrO2 at 900~1150 when heating or cooling may cause irregular deformation.

Fused cast AZS block can be used in areas in direct contact with molten metals and molten slags. It is the essential material used in the key areas that suffer from severe corrosion.



How to Store Ceramic Fiber Board

09:24, 24/2/2016 .. 0 comments .. Link

Ceramic fiber board is a high-strength refractory fiber board made of ceramic fiber. It is an essential high temperature refractory material. Ceramic fiber board must be stored properly to fulfill its high temperature properties.

Ceramic fiber board is made of ceramic fiber cotton by vacuum forming. It has tough texture, high strength, superior high temperature performance, excellent support force, good tensile strength and impact resistance. Its strength is better than the fiber blanket and vacuum formed felt. It will be gathered together when contact with water and its hardness will be decreased. In this case, it is easy to fall off when touched. So, waterproofing is very important for the storage of ceramic fiber board.

Ceramic fiber board should be stored in dry circumstances with no water and moisture. The building should be watertight and kept dry. Ceramic fiber board should have waterproof plastic film inside and be covered with cartons and placed on the ground with pallets. It should be placed on pallets without contact with the ground, at least 20 mm away from the ground. In the rain season, ceramic fiber products should be covered with a waterproof canvas. Pay attention to water leakage if it is stored in iron house.



How to Select Insulation Bricks

08:30, 15/2/2016 .. 0 comments .. Link

The use of insulation bricks in the thermal equipment can greatly reduce the heat loss and the weight of furnaces and improve the thermal efficiency and labor productivity.

For most thermal equipment, in order to save energy and improve the working conditions, insulation is necessary. However, for some equipment, insulation is not necessary, given the pros and cons of insulation. Therefore, the actual conditions and the properties of insulation bricks should be taken into consideration when selecting the right insulation bricks.

The insulation bricks can be divided into the following types:
1) Fire clay insulation brick GB/T 3994-2005
2) High alumina insulation brick
3) Mulite insulation brick

The principles for selecting insulation bricks include:
1) It should not affect the service life of the entire refractory masonry;
2) For continuously working high temperature furnaces, generally large area insulation is reasonable and can reduce the heat loss. However, for some special areas such as the open hearth roof, insulation may reduce the service life. For periodically working furnaces, regenerative heat loss is the main factor of heat loss. Insulation may increase the temperature of masonry and increase regenerative heat loss. So, whether periodically working furnaces should be insulated is determined after calculating the heat storage and heat loss.
3) Since the insulation bricks have high porosity, they cannot withstand too much load and should not directly contact the molten metals, molten slags and high-temperature dust.
4) Insulation bricks have low strength. The brick joints and expansion joints should be properly disposed avoid the damage caused by volume expansion. Insulating firebrick should not be subjected to intense mechanical vibration, shock and friction;
5) Since insulation bricks have big reheating linear shrinkage, the maximum working temperature should be 100 less than the firing temperature.



Common Refractories Used In the Glass Industry

08:11, 26/1/2016 .. 0 comments .. Link

Compared to the traditional processing, modern glass making technology has undergone a qualitative change in efficiency, energy consumption and quality. Furnaces, as the core equipment of glass making, continue to be improved. The rapid development of glass making promotes the development of refractories.

Refractories used in the glass furnace are required to withstand higher temperature, sharper temperature changes, more serious chemical corrosion and severer stress damage. The common refractories used in the glass furnace are as followings:

1) Fused cast AZS and fused cast high zircon block
For fused cast AZS block, it is important to improve its corrosion resistance and wear resistance. Besides the oxidizing melting method, reducing the carbon content to 0.005 and improving the exudation temperature of glass phase to 1450, the casting method and annealing method are also improved to improve the quality and properties of fused cast AZS.
Fused cast high zircon block with more than 90% ZrO2 has excellent thermal shock resistance and low potential of pollution to glass.

2) Chrome brick
Dense chrome bricks made by isostatic pressing are used in the walls, throat and other severely corroded areas in the E or C glass furnaces. Its service life can be as long as 6-7 years. Cr2O3 are added into fused cast AZS block to make fused cast AZSC block (Al2O3-ZrO2-SiO2-Cr2O3). At high temperature, Cr2O3 can from solid solution with Al2O3. Since Cr2O3 has a high melting point, it can improve the viscosity of glass phase and the exudation temperature of glass phase and improve the corrosion resistance to glass.

3) Basic brick
High pure direct bond basic bricks fired at 1800 are widely used in the walls of regerators and crown.

4) Olivine magnesia brick
Since olivine bonding phase has high corrosion resistance, increasing the olivine content in the bonding phase of magnesia can greatly improve the corrosion resistance of magnesia brick. Olivine magnesia brick is cheap and widely used in the middle part of the checker work.

5) Celsian olivine brick
Olivine has good corrosion resistance but insufficient thermal shock resistance. Celsian can significantly improve the thermal shock resistance. Celsian is formed in the firing process, and exists only in the binding matrix phase. Celsian can resist the corrosion of alkali and sulphate.

6) Monolithic materials
The application of monolithic materials in the glass industry can greatly reduce the joints of furnace structure and the cold repair time.



{ Last Page } { Page 1 of 5 } { Next Page }

About Me

Home
My Profile
Archives
Friends
My Photo Album

Links


Categories


Recent Entries

What are the unique advantages of Sillimanite Brick?
The characteristics and application scope of Ceramic Fiber Board
The Manufcturing Process Of Fire Clay Bricks
Four Factors For The Production Of Magnesia Carbon Brick
How To Judge The Quality Of Fire Clay Brick